WNM400(WUSTEEL) is a high-grade quenched and tempered wear-resistant steel plate produced by WuSteel; its grade is higher than WNM360.
WUSTEELWUSTEEL: Mainly used for structural steel plates used in the processing and manufacturing of wear-resistant and vulnerable parts for mines, coal mines, environmental protection, ventilation equipment, dump trucks and various construction machinery.
Grade representation method: The steel plate grade is composed of four parts representing the manufacturer, use, hardness and quality grade in order, for example: WNM400A, WNM400B, etc.
Symbol: W—–represents the first letter of the Chinese pinyin of “Wu” of WuSteel;
NM —-The first letter of the Chinese pinyin of the characters “Nai” and “M” for wear-resistant purposes;
A and B–respectively quality grades, meanwhile, A represents that the steel plate is not impacted, and B represents that the steel plate is impacted at 20 degrees normal temperature;
The steel plate adopts straight edge rolling, the head and tail are cut, and the two longitudinal sides are not cut, and the trimming margin is controlled according to the normal trimming plate.
The remaining size, shape, weight and allowable deviation of the steel plate shall comply with GB/T709.
The chemical composition of WNM400 (melting analysis) meets the requirements of the following table:
Pelat Baja Tahan Aus WNM400
WNM400 Chemical Composition:
Nilai
C
Dan
M N
P
S
Mo
Cr
Ni
B
A
0,25
0,70
1.60
0,025
0.010
0,50
Huruf pertama dari pinyin Cina dari karakter
Huruf pertama dari pinyin Cina dari karakter
B
0,25
0,70
1.60
0,025
0.010
0,50
Huruf pertama dari pinyin Cina dari karakter
Huruf pertama dari pinyin Cina dari karakter
Huruf pertama dari pinyin Cina dari karakter
Note: It is permissible to add microalloy strengthening elements to steel plates, such as Nb, V, Ti, etc.
Smelting method: electric furnace + refining outside the furnace.
Delivery status: quenching + tempering.
Mechanical properties:
The mechanical properties meet the requirements of the following table:
tungku listrik
Hardness (HBW)
20°CAKV longitudinal J
A
350~400
tungku listrik
B
350~400
= Tebal atau diameter kawat dalam mm
The surface quality of the steel plate meets the requirements of GB3274.
The inspection items, number of samples, sampling methods and test methods of each batch of steel plates shall meet the requirements of the following table:
tungku listrik
tungku listrik
tungku listrik
tungku listrik
tungku listrik
1
tungku listrik
1
tungku listrik
tungku listrik
2
tungku listrik
3
tungku listrik
tungku listrik
3
tungku listrik
1
tungku listrik
tungku listrik
4
kekerasan
1
tungku listrik
tungku listrik
Brinell hardness (HBW) inspection, according to the national standard GB/T231, the surface of the steel plate is milled off 1.0-2.2 mm, and then the hardness is tested on this surface.
The packaging, marking and quality certificate of the steel plate shall meet the requirements of GB/T247.
Comparison of WNM400 wear-resistant steel plate and imported steel:
Perbandingan pelat baja tahan aus WNM400 dan baja impor
Perbandingan pelat baja tahan aus WNM400 dan baja impor
Perbandingan pelat baja tahan aus WNM400 dan baja impor
Perbandingan pelat baja tahan aus WNM400 dan baja impor
400V
Perbandingan pelat baja tahan aus WNM400 dan baja impor
Application and prospect of WNM400 project:
Construction machinery, mining machinery, coal mining machinery, environmental protection machinery, metallurgical machinery and other manufacturing companies WuSteel cooperate in the production of excavators, loaders, bulldozers, bucket plates, blade plates, side blade plates, blades, crusher liners, and blade construction.
The project’s WNM400 is about 5000 tons. The prospects for exporting to the United States, Canada, Australia, India, and Europe are promising. More than 20,000 tons have been directly supplied to European customers.
WuSteel’s production technology is leading. The conventional specifications of WuSteel products have a thickness of 8-100mm, and most of them are 2000*8000 and 2200*8000.
Cutting method:
Metode pemotongan
Metode pemotongan pemotonganincludes water jet cutting, shearing, sawing or abrasive cutting.
Advantages: cutting heat has little effect, preventing the hardness of the entire workpiece from decreasing, and reducing the deformation of the cutting workpiece.
Disadvantages: high cost, only thin plates can be cut, and the cutting speed is slow.
Metode pemotongan
Thermal cutting includes oxygen fuel flame cutting (hereinafter referred to as “flame cutting”), isoparticle cutting and laser cutting.
Advantages: cutting cost is low, processing equipment is available everywhere, it can cut thick plates, and the cutting speed is fast.
Disadvantages: easy to reduce the hardness of the steel plate and cause cracks.
Metode pemotongan
Metode pemotongan
One of the ways to avoid cutting cracks, if the whole board cannot be preheated, partial preheating can also be used instead. Use low-speed cutting to prevent cutting cracks, and its reliability is not as good as preheating. I suggest preheating the cutting tape (around or straight line of the workpiece) with flame gun cavitation several times before cutting, and the preheating temperature should reach 100℃. If the cutting equipment is double guns or multiple guns, the front flame gun can be used to raise the height for preheating, and the back flame gun can cut, which can also achieve the purpose of preheating cutting.
Gunakan pemotongan kecepatan rendah untuk mencegah pemotongan retak
Regardless of whether the cut piece is preheated or not, the slow cooling of the steel plate after cutting will effectively reduce the risk of cracks after cutting. If the workpiece is stacked with warm after cutting and covered with a heat insulation blanket, slow cooling can also be achieved, and slow cooling requires cooling to room temperature.
pendinginan lambat juga dapat dicapai
For the cutting of wear-resistant plates, heating (pendinginan lambat juga dapat dicapai) immediately after cutting can also be an effective method and measure to prevent cutting cracks. After the steel plate is cut, the low temperature tempering treatment can effectively eliminate the residual internal stress of the cutting.
For the method of heating the steel plate after cutting, the heating method of flame gun burning, electronic heating blanket and heating furnace can also be used for heating after cutting.
Untuk memberikan pengalaman terbaik, kami menggunakan teknologi seperti cookie untuk menyimpan dan/atau mengakses informasi perangkat. Menyetujui teknologi ini akan memungkinkan kami memproses data seperti perilaku penjelajahan atau ID unik di situs ini. Tidak menyetujui atau menarik persetujuan, dapat berdampak buruk pada fitur dan fungsi tertentu.
Fungsional
Selalu aktif
Penyimpanan atau akses teknis sangat diperlukan untuk tujuan sah yang memungkinkan penggunaan layanan tertentu yang secara eksplisit diminta oleh pelanggan atau pengguna, atau untuk tujuan semata-mata melakukan transmisi komunikasi melalui jaringan komunikasi elektronik.
Preferensi
Penyimpanan atau akses teknis diperlukan untuk tujuan sah menyimpan preferensi yang tidak diminta oleh pelanggan atau pengguna.
Statistik
Penyimpanan atau akses teknis yang digunakan secara eksklusif untuk tujuan statistik.Penyimpanan atau akses teknis yang digunakan secara eksklusif untuk tujuan statistik anonim. Tanpa panggilan pengadilan, kepatuhan sukarela dari Penyedia Layanan Internet Anda, atau catatan tambahan dari pihak ketiga, informasi yang disimpan atau diambil untuk tujuan ini saja biasanya tidak dapat digunakan untuk mengidentifikasi Anda.
Pemasaran
Penyimpanan atau akses teknis diperlukan untuk membuat profil pengguna untuk mengirim iklan, atau untuk melacak pengguna di situs web atau di beberapa situs web untuk tujuan pemasaran serupa.