Inconel
Inconel ialah keluarga aloi super berasaskan nikel-kromium austenit.
Komposisi Inconel
| Inconel | Unsur (% mengikut jisim) | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Dalam | Cr | Fe | Mo | Nb | Co | Mn | Cu | Al | Daripada | Dan | C | S | P | B | |
| 600 | 72.0 | 14.0–17.0 | 6.0–10.0 | 1.0 | 0.5 | 0.5 | 0.15 | 0.015 | |||||||
| 617 | 44.2–56.0 | 20.0–24.0 | 3.0 | 8.0–10.0 | 10.0–15.0 | 0.5 | 0.5 | 0.8–1.5 | 0.6 | 0.5 | 0.15 | 0.015 | 0.015 | 0.006 | |
| 625 | 58.0 | 20.0–23.0 | 5.0 | 8.0–10.0 | 3.15–4.15 | 1.0 | 0.5 | 0.4 | 0.4 | 0.5 | 0.1 | 0.015 | 0.015 | ||
| 690 | 59.5 | 30 | 9.2 | 0.35 | 0.01 | 0.02 | 0.35 | 0.019 | 0.003 | ||||||
| 718 | 50.0–55.0 | 17.0–21.0 | imbangan | 2.8–3.3 | 4.75–5.5 | 1.0 | 0.35 | 0.2–0.8 | 0.65–1.15 | 0.3 | 0.35 | 0.08 | 0.015 | 0.015 | 0.006 |
| X-750 | 70.0 | 14.0–17.0 | 5.0–9.0 | 0.7–1.2 | 1.0 | 1.0 | 0.5 | 0.4–1.0 | 2.25–2.75 | 0.5 | 0.08 | 0.01 | |||
Aloi Inconel
Aloi inconel termasuk:
- Inconel 600: Penyelesaian pepejal diperkukuh
- Inconel 601
- Inconel 625: Tahan asid, kebolehkimpalan yang baik. Versi LCF biasanya digunakan dalam belos.
- Inconel 690: Kandungan kobalt rendah untuk aplikasi nuklear, dan kerintangan rendah
- Inconel 713C: Pemendakan boleh mengeras aloi tuangan asas nikel-kromium
- Inconel 718: Gamma dwi perdana diperkukuh dengan kebolehkimpalan yang baik
- Inconel 751: Peningkatan kandungan aluminium untuk kekuatan pecah yang lebih baik dalam julat 1600 °F
- Inconel 792: Peningkatan kandungan aluminium untuk sifat kakisan suhu tinggi yang dipertingkatkan, digunakan terutamanya dalam turbin gas
- Inconel 939: Gamma prima diperkukuh untuk meningkatkan kebolehkimpalan
Gred Setara Inconel
| STANDARD | BAHAN NO. | AS | GOST | AFNOR | DIA | BS | DALAM | ATAU |
|---|---|---|---|---|---|---|---|---|
| Aloi 600 | 2.4816 | N06600 | MNJMc 28-2.5-1.5 | NC15FE11M | NCF 600 | ITU 13 | NiCr15Fe | EI868 |
| Aloi 601 | 2.4851 | N06601 | XH60BT | NC23FeA | NCF 601 | ITU 49 | NiCr23Fe | EI868 |
| Aloi 617 | 2.4663 | N06617 | ||||||
| Aloi 625 | 2.4856 | N06625 | ХН75МБТУ | NC22DNB4M | NCF 625 | ITU 21 | NiCr22Mo9Nb | EI602 |
| Aloi 690 | 2.4642 | N06690 | ||||||
| Aloi 718 | 2.4668 | N07718 | ||||||
| Aloi 725 | – | N07725 | ||||||
| Aloi X-750 | 2.4669 | N07750 |
Takat Lebur Inconel, Ketumpatan dan Kekuatan Tegangan
| Ketumpatan | Takat Lebur | Kekuatan Tegangan | Kekuatan Hasil (0.2% Offset) | Pemanjangan | |
|---|---|---|---|---|---|
| 600 | 8.47 g/cm3 | 1413 °C (2580 °F) | Psi – 95,000, MPa – 655 | Psi – 45,000, MPa – 310 | 40% |
| 601 | 8.1 g/cm3 | 1411 °C (2571 °F) | Psi – 80,000, MPa – 550 | Psi – 30,000, MPa – 205 | 30% |
| 617 | 8.3g/cm³ | 1363°C | ≥ 485 MPa | ≥ 275 MPa | 25% |
| 625 | 8.4 g/cm3 | 1350 °C (2460 °F) | Psi – 135,000, MPa – 930 | Psi – 75,000, MPa – 517 | 42.5 % |
| 690 | 8.3g/cm³ | 1363°C | ≥ 485 MPa | ≥ 275 MPa | 25% |
| 718 | 8.2 g/cm3 | 1350 °C (2460 °F) | Psi – 135,000, MPa – 930 | Psi – 70,000, MPa – 482 | 45 % |
| 725 | 8.31 g/cm3 | 1271°C-1343°C | 1137 MPa | 827 MPa | 20% |
| X-750 | 8.28 g/cm3 | 1430°C | 1267 MPa | 868 MPa | 25% |
316 Keluli Tahan Karat
Keluli Tahan Karat 316 juga dikenali sebagai AISI 316. Keluli Tahan Karat 316 mempunyai rintangan kakisan yang lebih baik sedikit daripada 302 dan 304. Ia juga mempunyai sifat bukan magnet yang lebih baik.
Gred Setara SS 316
| STANDARD | BAHAN NO. | AS | DIA | BS | GOST | AFNOR | DALAM |
|---|---|---|---|---|---|---|---|
| SS 316 | 1.4401 / 1.4436 | S31600 | SUS 316 | 316S31 / 316S33 | – | Z7CND17-11-02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
Komposisi SS 316
| Gred | C | Mn | Dan | P | S | Cr | Mo | Dalam | N |
|---|---|---|---|---|---|---|---|---|---|
| SS 316 | 0.08 maks | 2 maks | 0.75 maks | 0.045 maks | 0.030 maks | 16 – 18 | 2 – 3 | 10 – 14 | 0.1 maks |
SS 316 Takat Lebur, Ketumpatan dan Kekuatan Tegangan
| Gred | Ketumpatan | Takat Lebur | Kekuatan Tegangan | Kekuatan Hasil (0.2% Offset) | Pemanjangan |
| SS 316 | 8.0 g/cm3 | 1454 °C (2650 °F) | Psi – 75000, MPa – 515 | Psi – 30000, MPa – 205 | 35 % |