Incoloy 901(UNS N09901/Din 1.4898 Alloy 901)

Incoloy 901 (UNS N09901/Din 1.4898),

Alloy 901(Incoloy) has good corrosion resistance to the atmospheres normally found in jet engine operations.

Incoloy 901 Chemical composition:

paduan	%	Ni	Dengan	Al	Fe	Anda	Bersama	M N	S	C	Dan	P	Cr	Mo	B
Incoloy 901	Min.	40.0				2.35							11.0	5.0	0.01
Incoloy 901	Max.	45.0	0.50	0.35	Keseimbangan	3.10	1.0	1.0	0.03	0.10	0.60	0.03	14.0	7.0	0.02

Incoloy 901 Physical properties:

Kepadatan	8.14 g/cm3
Titik lebur	1280-1345℃

Incoloy 901 minimum mechanical properties in the room temperature:

Status	Daya tarik Rm N/mm2	Kekuatan hasil RP0.2N/mm2	Pemanjangan A5 %
Incoloy 901	1034	689	12

Keterangan

A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.

Tahan korosi

Alloy 901 has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.

Kemungkinan untuk dilaksanakan
Kerja Panas

Alloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.

Kemampuan las

Alloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.

(Incoloy 901) Regular shape for all kinds of alloys
Membentuk	Spesifikasi	Formulir Pasokan	Yang lain
Lembaran	Thickness：0.40-4.75mm，General Width：1000、1219、1500mm	Seluruh Coil atau bagiannya	Cold Annealed，Surface 2B、2E
Piring	Thickness：4.76-60mm，Width：1500、2000、2500mm，Length：3000、6000、8000、8500mm（Under 10mm plate can be coiled）	Seluruh Coil atau bagiannya	Single hot rolling，Solid solution annealed state，Surface 1D
Sabuk	Thickness：0.10-3.0mm，Width：50-500mm	Seluruh Coil atau ukuran Tertentu	Cold Annealed，Surface 2B、2E
Bar & Rod	Rolled barΦ5-45mm，Length≤1500mm	Polished Bar（circle、Square）	Solution annealing,descaling
Bar & Rod	Forged barΦ26-245mm，Length≤4000mm	Polished Bar（circle、Square）	Solution annealing,descaling
tabung las	Outer diameterΦ4.76-135mm，Wall Thickness0.25-4.00mm，Length：≤35000 mm	Berdasarkan kebutuhan Anda
Tabung mulus	Outer diameterΦ3-114mm，Wall Thickness0.2-4.5mm	Berdasarkan kebutuhan Anda
Kabel	Diameter luar 0.1-13mm	Berdasarkan kebutuhan Anda	Ni & Ni alloy, Ti & Ti alloy
Potongan palsu	discs,rings,squares,blocks,slabs	Berdasarkan kebutuhan Anda	Steel, Alloy
flange	Semua jenis Flang	Berdasarkan kebutuhan Anda	Steel, Alloy
bahan las	Kawat koil 0.025mm-1.6mm	Berdasarkan kebutuhan Anda	Certificate of Origin：America, Sweden, Britain, Germany, Austria, Italy, France.
	Kawat Lurus 1.6mm-4.0mm
	Batang las 1.2mm-4.0mm
Tabung	Elbow, three links, four links, different diameter size	Berdasarkan kebutuhan Anda	Ni & Ni alloy, Ti & Ti alloy
Laminasi berikat eksplosif	Ketebalan Lembaran Mentah 2mm	Berdasarkan kebutuhan Anda	Ni & Ni alloy, Ti & Ti alloy