Inconel
Inconel adalah keluarga superalloy berbasis nikel-kromium austenitik.
Komposisi Inkonel
| Inconel | Elemen (% berdasarkan massa) | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Ni | Cr | Fe | Mo | Nb | Bersama | M N | Dengan | Al | Anda | Dan | C | S | P | B | |
| 600 | 72.0 | 14.0–17.0 | 6.0–10.0 | 1.0 | 0.5 | 0.5 | 0.15 | 0.015 | |||||||
| 617 | 44.2–56.0 | 20.0–24.0 | 3.0 | 8.0–10.0 | 10.0–15.0 | 0.5 | 0.5 | 00,8–1,5 | 0.6 | 0.5 | 0.15 | 0.015 | 0.015 | 0.006 | |
| 625 | 58.0 | 20.0–23.0 | 5.0 | 8.0–10.0 | 3.15–4.15 | 1.0 | 0.5 | 0.4 | 0.4 | 0.5 | 0.1 | 0.015 | 0.015 | ||
| 690 | 59.5 | 30 | 9.2 | 0.35 | 0.01 | 0.02 | 0.35 | 0.019 | 0.003 | ||||||
| 718 | 50,0–55,0 | 17.0–21.0 | keseimbangan | 2.8–3.3 | 4.75–5.5 | 1.0 | 0.35 | 0.2–0.8 | 00,65–1,15 | 0.3 | 0.35 | 0.08 | 0.015 | 0.015 | 0.006 |
| X-750 | 70.0 | 14.0–17.0 | 5.0–9.0 | 0.7–1.2 | 1.0 | 1.0 | 0.5 | 0.4–1.0 | 2,25–2,75 | 0.5 | 0.08 | 0.01 | |||
Paduan inkonel
Paduan inconel meliputi:
- Inconel 600: Solusi padat diperkuat
- Inkonel 601
- Inconel 625: Tahan asam, kemampuan las yang baik. Versi LCF biasanya digunakan pada bellow.
- Inconel 690: Kandungan kobalt rendah untuk aplikasi nuklir, dan resistivitas rendah
- Inconel 713C: Paduan cor berbahan dasar nikel-kromium yang dapat diperkeras dengan presipitasi
- Inconel 718: Gamma double prime diperkuat dengan kemampuan las yang baik
- Inconel 751: Peningkatan kandungan aluminium untuk meningkatkan kekuatan pecah pada kisaran 1600 °F
- Inconel 792: Peningkatan kandungan aluminium untuk meningkatkan sifat korosi suhu tinggi, terutama digunakan pada turbin gas
- Inconel 939: Gamma prime diperkuat untuk meningkatkan kemampuan las
Nilai Setara Inconel
| STANDAR | BAHAN NO. | KITA | gost | AFNOR | JIS | BS | PADA | ATAU |
|---|---|---|---|---|---|---|---|---|
| Paduan 600 | 2.4816 | N06600 | MNJMc 28-2.5-1.5 | NC15FE11M | NCF 600 | ITU 13 | NiCr15Fe | EI868 |
| Paduan 601 | 2.4851 | N06601 | XH60BT | NC23FeA | NCF 601 | ITU 49 | NiCr23Fe | EI868 |
| Paduan 617 | 2.4663 | N06617 | ||||||
| Paduan 625 | 2.4856 | N06625 | ХН75МБТУ | NC22DNB4M | NCF 625 | ITU 21 | NiCr22Mo9Nb | EI602 |
| Paduan 690 | 2.4642 | N06690 | ||||||
| Paduan 718 | 2.4668 | N07718 | ||||||
| Paduan 725 | - | N07725 | ||||||
| Paduan X-750 | 2.4669 | N07750 |
Titik Leleh Inconel, Kepadatan dan Kekuatan Tarik
| Kepadatan | Titik lebur | Daya tarik | Kekuatan Hasil (Offset 0,2%) | Pemanjangan | |
|---|---|---|---|---|---|
| 600 | 8,47 gram/cm3 | 1413 °C (2580 °F) | Psi – 95.000, MPa – 655 | Psi – 45.000, MPa – 310 | 40% |
| 601 | 8,1 gram/cm3 | 1411 °C (2571 °F) | Psi – 80.000, MPa – 550 | Psi – 30.000, MPa – 205 | 30% |
| 617 | 8,3g/cm³ | 1363°C | ≥ 485 MPa | ≥ 275 MPa | 25% |
| 625 | 8,4 gram/cm3 | 1350 °C (2460 °F) | Psi – 135.000, MPa – 930 | Psi – 75.000, MPa – 517 | 42,5% |
| 690 | 8,3g/cm³ | 1363°C | ≥ 485 MPa | ≥ 275 MPa | 25% |
| 718 | 8,2 gram/cm3 | 1350 °C (2460 °F) | Psi – 135.000, MPa – 930 | Psi – 70.000, MPa – 482 | 45% |
| 725 | 8,31 gram/cm3 | 1271°C-1343 °C | 1137 MPa | 827 MPa | 20% |
| X-750 | 8,28 gram/cm3 | 1430°C | 1267 MPa | 868 MPa | 25% |
316 Baja Tahan Karat
Stainless Steel 316 juga dikenal sebagai AISI 316. Stainless Steel 316 memiliki ketahanan korosi yang sedikit lebih baik dibandingkan 302 dan 304. Ia juga memiliki sifat non-magnetik yang lebih baik.
Nilai Setara SS 316
| STANDAR | BAHAN NO. | KITA | JIS | BS | gost | AFNOR | PADA |
|---|---|---|---|---|---|---|---|
| SS 316 | 1.4401 / 1.4436 | S31600 | SUS 316 | 316S31 / 316S33 | - | Z7CND17‐11‐02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
Komposisi SS 316
| Nilai | C | M N | Dan | P | S | Cr | Mo | Ni | adalah Baja Struktural Kekuatan Tinggi Paduan Rendah Standar GB Cina |
|---|---|---|---|---|---|---|---|---|---|
| SS 316 | 00,08 maks | 2 maks | 00,75 maks | 00,045 maks | 00,030 maks | 16 – 18 | 2 – 3 | 10 – 14 | 00,1 maks |
SS 316 Titik Lebur, Massa Jenis dan Kekuatan Tarik
| Nilai | Kepadatan | Titik lebur | Daya tarik | Kekuatan Hasil (Offset 0,2%) | Pemanjangan |
| SS 316 | 8,0 gram/cm3 | 1454 °C (2650 °F) | Psi – 75000, MPa – 515 | Psi – 30000, MPa – 205 | 35% |