This document provides a comprehensive comparison between the UNSBab 95500and UNSBab 95400copper alloys, detailing their chemical composition, mechanical properties, temperature performance, industry applications, shapes and sizes, production standards, processing techniques, advantages and disadvantages, and similar products, all presented in table formats.
Komposisi kimia
Elemen
UNS C95500 Content (%)
UNS C95400 Content (%)
Copper, Cu
78.0
83.0
Aluminium, Al
10.0 – 11.5
10.0
Nikel, Ni
3.0 – 5.50
1.0 – 1.5
Besi, Fe
3.0 – 5.0
3.0 – 5.0
Manganese, Mn
3.50
0.5
Peralatan mekanis
UNS C95500
Milik
Metrik
Imperial
Hardness, Brinell (sand cast)
192
192
Daya tarik
585 – 660 MPa
84800 – 95700 psi
Kekuatan hasil
240 – 360 MPa
34800 – 52200 psi
Elongation at Break
5.00% – 25.00%
5.00% – 25.00%
Compressive Strength
240 – 690 MPa
34800 – 100000 psi
UNS C95400
Milik
Metrik
Imperial
Hardness, Brinell
170 – 210
170 – 210
Daya tarik
380 – 550 MPa
55000 – 80000 psi
Kekuatan hasil
200 – 300 MPa
29000 – 43500 psi
Elongation at Break
10.00% – 30.00%
10.00% – 30.00%
Compressive Strength
200 – 500 MPa
29000 – 72500 psi
Performa pada Suhu Berbeda
Milik
Bab 95500
Bab 95400
Thermal Expansion Coefficient
16.2 µm/m°C
16.5 µm/m°C
Konduktivitas termal
42.0 W/mK
35.0 W/mK
Aplikasi Industri
Aplikasi
Bab 95500
Bab 95400
Marine Components
Shafting, fittings
Propellers, valves
Listrik
Electrical connectors
Electrical components
Otomotif
Transmission parts
Gears and bushings
Shapes and Sizes
Membentuk
Bab 95500
Bab 95400
Standard Forms
Rods, tubes, castings
Rods, plates, tubes
Custom Sizes
Available on request
Available on request
Standar Produksi
Standar
Bab 95500
Bab 95400
ASMA
B148, B271
B148, B271
MIL
Tidak berlaku
MIL B-24480
Processing Techniques
Pengelasan
Teknik
Bab 95500
Bab 95400
Preferred Methods
Brazing, soldering
Brazing, soldering
Tidak direkomendasikan
Pengelasan oksiasetilen
Pengelasan oksiasetilen
Kemampuan mesin
Alloy Rating (C36000 = 100)
Bab 95500
Bab 95400
Peringkat Kemampuan Mesin
50%
60%
Perawatan panas
Perawatan panas
Bab 95500
Bab 95400
Stress Relieving Temperature
316°C (600°F)
316°C (600°F)
Reaction to Heat Treatment
Does not react significantly
Slight improvement in strength
Keuntungan dan Kerugian
Bab 95500
Keuntungan
Metode pemotongan
High strength and hardness
Higher cost per unit
Good fatigue resistance
More complex processing
Bab 95400
Keuntungan
Metode pemotongan
Ketahanan korosi yang sangat baik
Lower strength than C95500
Kemampuan mesin yang baik
Limited applications in high-stress environments
Similar Products
Similar Products
Bab 95500
Bab 95400
Other Copper Alloys
C95600, C95200
C95200, C93200
Bronze Alloys
Aluminum bronze, tin bronze
Aluminum bronze, tin bronze
This comparison provides a detailed overview of the properties and characteristics of UNS C95500 and UNS C95400 copper alloys, assisting in material selection for specific applications. If you have further inquiries or require additional information, please feel free to ask!
itu masuk ke zona suhu tinggi di mana struktur matriksnya adalah fase tunggal austenit
Untuk memberikan pengalaman terbaik, kami menggunakan teknologi seperti cookie untuk menyimpan dan/atau mengakses informasi perangkat. Menyetujui teknologi ini akan memungkinkan kami memproses data seperti perilaku penjelajahan atau ID unik di situs ini. Tidak menyetujui atau menarik persetujuan, dapat berdampak buruk pada fitur dan fungsi tertentu.
Fungsional
Selalu aktif
Penyimpanan atau akses teknis sangat diperlukan untuk tujuan sah yang memungkinkan penggunaan layanan tertentu yang secara eksplisit diminta oleh pelanggan atau pengguna, atau untuk tujuan semata-mata melakukan transmisi komunikasi melalui jaringan komunikasi elektronik.
Preferensi
Penyimpanan atau akses teknis diperlukan untuk tujuan sah menyimpan preferensi yang tidak diminta oleh pelanggan atau pengguna.
Statistik
Penyimpanan atau akses teknis yang digunakan secara eksklusif untuk tujuan statistik.Penyimpanan atau akses teknis yang digunakan secara eksklusif untuk tujuan statistik anonim. Tanpa panggilan pengadilan, kepatuhan sukarela dari Penyedia Layanan Internet Anda, atau catatan tambahan dari pihak ketiga, informasi yang disimpan atau diambil untuk tujuan ini saja biasanya tidak dapat digunakan untuk mengidentifikasi Anda.
Pemasaran
Penyimpanan atau akses teknis diperlukan untuk membuat profil pengguna untuk mengirim iklan, atau untuk melacak pengguna di situs web atau di beberapa situs web untuk tujuan pemasaran serupa.