Inconel
Inconel es una familia de superaleaciones austeníticas a base de níquel-cromo.
Composición de Inconel
| Inconel | Elemento (% en masa) | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Ni | Cr | Fe | Mes | Nótese bien | Co | Minnesota | Con | Alabama | usted | Y | C | S | PAG | B | |
| 600 | 72.0 | 14,0–17,0 | 6,0–10,0 | 1.0 | 0.5 | 0.5 | 0.15 | 0.015 | |||||||
| 617 | 44,2–56,0 | 20,0–24,0 | 3.0 | 8,0–10,0 | 10,0–15,0 | 0.5 | 0.5 | 0.8–1.5 | 0.6 | 0.5 | 0.15 | 0.015 | 0.015 | 0.006 | |
| 625 | 58.0 | 20,0–23,0 | 5.0 | 8,0–10,0 | 3,15–4,15 | 1.0 | 0.5 | 0.4 | 0.4 | 0.5 | 0.1 | 0.015 | 0.015 | ||
| 690 | 59,5 | 30 | 9.2 | 0.35 | 0.01 | 0.02 | 0.35 | 0.019 | 0.003 | ||||||
| 718 | 50,0–55,0 | 17,0–21,0 | balance | 2,8–3,3 | 4,75–5,5 | 1.0 | 0.35 | 0.2–0.8 | 0.65–1.15 | 0.3 | 0.35 | 0.08 | 0.015 | 0.015 | 0.006 |
| X-750 | 70.0 | 14,0–17,0 | 5,0–9,0 | 0.7–1.2 | 1.0 | 1.0 | 0.5 | 0.4–1.0 | 2,25–2,75 | 0.5 | 0.08 | 0.01 | |||
aleaciones de inconel
Las aleaciones de inconel incluyen:
- Inconel 600: Solución sólida reforzada
- Inconel 601
- Inconel 625: Resistente a los ácidos, buena soldabilidad. La versión LCF se utiliza normalmente en fuelles.
- Inconel 690: Bajo contenido de cobalto para aplicaciones nucleares y baja resistividad
- Inconel 713C: aleación fundida a base de níquel-cromo endurecible por precipitación
- Inconel 718: Gamma doble prima reforzada con buena soldabilidad
- Inconel 751: mayor contenido de aluminio para mejorar la resistencia a la rotura en el rango de 1600 °F
- Inconel 792: mayor contenido de aluminio para mejorar las propiedades de corrosión a alta temperatura, utilizado especialmente en turbinas de gas
- Inconel 939: Gamma Prime reforzado para aumentar la soldabilidad
Grados equivalentes de Inconel
| ESTÁNDAR | NÚMERO MATERIAL. | nosotros | GOST | AFNOR | JIS | BS | EN | O |
|---|---|---|---|---|---|---|---|---|
| Aleación 600 | 2.4816 | N06600 | MNJMc 28-2.5-1.5 | NC15FE11M | 600 FNC | ESE 13 | NiCr15Fe | EI868 |
| Aleación 601 | 2.4851 | N06601 | XH60BT | NC23FeA | NCF 601 | ESO ES 49 | NiCr23Fe | EI868 |
| Aleación 617 | 2.4663 | N06617 | ||||||
| Aleación 625 | 2.4856 | N06625 | ХН75МБТЮ | NC22DNB4M | FNC 625 | ESO ES 21 | NiCr22Mo9Nb | EI602 |
| Aleación 690 | 2.4642 | N06690 | ||||||
| Aleación 718 | 2.4668 | N07718 | ||||||
| Aleación 725 | - | N07725 | ||||||
| Aleación X-750 | 2.4669 | N07750 |
Punto de fusión, densidad y resistencia a la tracción del Inconel
| Densidad | Punto de fusion | Fuerza de Tensión | Límite elástico (0,2 % de compensación) | Alargamiento | |
|---|---|---|---|---|---|
| 600 | 8,47 g/cm3 | 1413°C (2580°F) | Psi – 95.000, MPa – 655 | Psi – 45.000, MPa – 310 | 40 % |
| 601 | 8,1g/cm3 | 1411°C (2571°F) | Psi – 80.000, MPa – 550 | Psi – 30.000, MPa – 205 | 30 % |
| 617 | 8,3 g/cm³ | 1363°C | ≥ 485MPa | ≥ 275MPa | 25 % |
| 625 | 8,4 g/cm3 | 1350°C (2460°F) | Psi – 135.000, MPa – 930 | Psi – 75.000, MPa – 517 | 42,5% |
| 690 | 8,3 g/cm³ | 1363°C | ≥ 485MPa | ≥ 275MPa | 25 % |
| 718 | 8,2 g/cm3 | 1350°C (2460°F) | Psi – 135.000, MPa – 930 | Psi – 70.000, MPa – 482 | 45 % |
| 725 | 8,31 g/cm3 | 1271°C-1343°C | 1137MPa | 827MPa | 20 % |
| X-750 | 8,28g/cm3 | 1430°C | 1267 MPa | 868MPa | 25 % |
Acero inoxidable 316
El acero inoxidable 316 también se conoce como AISI 316. El acero inoxidable 316 tiene una resistencia a la corrosión ligeramente mejor que el 302 y el 304. También tiene mejores propiedades no magnéticas.
Grados equivalentes a SS 316
| ESTÁNDAR | NÚMERO MATERIAL. | nosotros | JIS | BS | GOST | AFNOR | EN |
|---|---|---|---|---|---|---|---|
| SS 316 | 1,4401 / 1,4436 | S31600 | SUS 316 | 316S31 / 316S33 | - | Z7CND17‐11‐02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
Composición SS 316
| Calificación | C | Minnesota | Y | PAG | S | Cr | Mes | Ni | norte |
|---|---|---|---|---|---|---|---|---|---|
| SS 316 | 00,08 máx. | 2 máximo | 0.75 máx. | 00,045 máx. | 0.030 máx. | 16 – 18 | 2 – 3 | 10 – 14 | 0.1 máx. |
SS 316 Punto de fusión, densidad y resistencia a la tracción
| Calificación | Densidad | Punto de fusion | Fuerza de Tensión | Límite elástico (0,2 % de compensación) | Alargamiento |
| SS 316 | 8,0 g/cm3 | 1454°C (2650°F) | Psi – 75000, MPa – 515 | Psi – 30000, MPa – 205 | 35 % |